纳米复合高吸收铬鞣助剂在牛皮鞣制中的应用Application of Nano-composite High Exhaustion Chrome Tanning Auxiliaries on Cattle Leather Clean Tanning Process
高党鸽,吕秀娟,马建中,李运,吕斌
Gao Dangge,Lv Xiujuan,Ma Jianzhong,Li Yun,Lv Bin
摘要(Abstract)：
将纳米复合高吸收铬鞣助剂(KR-T113)应用于牛沙发革的清洁化鞣制中,采用5.0%KR-T113配合3.0%铬粉分别对软化皮和酸皮进行鞣制,考察了KR-T113对鞣制后坯革应用性能的影响。结果表明:鞣制后蓝湿革的收缩温度均为95℃,废液中的Cr2O3含量均为0.02g/L,与采用7.0%铬粉常规鞣制废液相比,大幅降低了废液中的铬含量;坯革的物理机械性能与常规铬鞣革相近,手感紧实、填充性能较好,并且对酸皮鞣制后的坯革柔软度比常规铬鞣革提高了2.5%。扫描电镜结果表明:KR-T113的引入能够有效提高纤维的分散性能,同时未破坏胶原的微观结构。
Nano-composite high exhaustion chrome tanning auxiliaries( KR-T113) were applied in cattle furniture leather clean tanning process. The bated hide and pickled hide were tanned by 5. 0% KR-T113 associated with 3. 0% chromate separately. The effects of KR-T113 on application performance of wet blues were investigated. The application results show that the shrinkage temperature( Ts) of both of wet blues is 95℃. The Cr2O3content in wastewater is 0. 02g / L,which reduces the chromium content of wastewater significantly compared with that of coventional chrome tanned leather tanned by 7. 0% chromate. The mechanical properties of crust leathers are close to that of coventional chrome tanned leather and the addition of KR-T113 could endow resultant leather with good handle and filling properties. In comparison with coventional chrome tanned leather,the softness of crust leather which was made from pickled hide is increased by 2. 5%. The Scanning Electron Microscopy( SEM) results show that the introduction of KR-T113 could effectively improve the dispersion properties of fibers and does not destroy the microstructure structure of collagen.
关键词(KeyWords)：
纳米复合高吸收铬鞣助剂;牛皮;鞣制;清洁化制革
nano-composite high exhaustion chrome tanning auxiliaries;cattle;cleaning tanning process
基金项目(Foundation): 国家重点基础研究发展计划(973计划前期研究专项)(2011CB612309);; 国家自然基金青年科学基金项目(21104042)
作者(Author):
高党鸽,吕秀娟,马建中,李运,吕斌
Gao Dangge,Lv Xiujuan,Ma Jianzhong,Li Yun,Lv Bin
DOI: 10.13536/j.cnki.issn1001-6813.2013.19.020
参考文献(References)：
- [1]蔡启祥,李临生,兰云军.二羧酸单甲酯盐的制备及其在铬鞣中的应用研究[J].皮革科学与工程,2002,12(2):36-40
- [2]Bowes J H,Elliot R G H.Tanning with formaldehyde in the presence of organic compounds[J].Journal of the Society of Lether Technologists and Chemists,1962(57):374-391
- [3]白云翔,王鸿儒.醛酸型铬鞣助剂SYY的结构及应用研究[J].中国皮革,2002,20(4):12-17
- [4]Sundarapandiyan S,Patrick E Brutto,Siddhartha G.Enhancement of chromium uptake in tanning using oxazolidine[J].Journal of Hazardous Materials,2012(190):802-809
- [5]Kanagaraj J,Sadulla S,Jawahar M,et al.Interaction of aldehyde developed from amino acids of tannery waste in a lower-chrome tannage:An eco-friendly approach[J].Journal of the society of Lether Technologists and Chemists,2005,89:18-27
- [6]Wang H R,Zhou X.A new pretanning agent for high exhaustion chrom tannage[J].Journal of the Society of Lether Technologists and Chemists,2005,89:117-120
- [7]栾世方,石碧,范浩军,等.大分子铬鞣助剂的多官能团对铬吸收及成革性能的影响[J].中国皮革,2003,32(21):24-28
- [8]Kanagaraj J,Sanjeev G.High exhaust chrome tanning using novel copolymer for ecofriendly leather processing[J].Journal of the Society of Leather Technologists and Chemists,2008,103(1):36-43
- [9]朱正鑫,李魏,戴红.乙二醛、丙烯酸及胶原水解物制备铬鞣助剂[J].皮革科学与工程,2012,22(2):19-25
- [10]强西怀,安军,管建.端羟基超支化聚合物助鞣剂的合成及应用[J].精细化工,2008,25(9):900-903
- [11]马建中,李运,高党鸽.P(DMDAACAA-AM-HEA)的制备及在皮革鞣制中的应用[J].功能材料,2011,8(5):13-16
- [12]储云.乙烯基聚合物/蒙脱土纳米复合鞣剂的制备、结构及性能研究[D].陕西科技大学,2005
- [13]马建中,高党鸽,李运,等.聚二烯丙基二甲基氯化铵-丙烯酰胺-乙二醛/纳米插层复合蒙脱石的制备及性能[J].硅酸盐学报,2008,36(6):844-849
- [14]彭章义,杜光伟,周绍兵.含N-羟甲基的两性两亲聚合物有机鞣剂的研究[M].第四届亚洲国际皮革科学技术会议论文集,北京,1988:119-121
- [15]李志强,廖隆理.生皮化学与组织学[M].北京:中国轻工业出版社,2010
- [16]Su Dihan,Wang Chunhua,Ca Sumei,et al.Influence of palygorskite on the structure and thermal stability of collagen[J].Applied Clay Science,2012(62-63):41-46